點(diǎn)擊圖片查看大圖| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 |
| 成型收縮率 | UBEmethod | 1.5 | % | |
| 吸水率 | ASTM D-570 | 1.8 | % | |
| 成型收縮率 | UBEmethod | 1.4 | % | |
| 吸水率 | ASTM D-570 | 10.7 | % | |
| 比重 | ASTM D-792 | 1.14 | ||
| TABER磨耗率 | ASTM D-1044 | 7 | mg | |
| 屈服下的伸張強(qiáng)度 | 23° | ASTM D-638 | 400 | kgf/cm2 |
| 彎曲強(qiáng)度 | -30° | ASTM D-790 | 1300 | kgf/cm2 |
| 擠剪強(qiáng)度 | 23° | ASTM D-732 | 600 | kgf/cm2 |
| 屈服下的伸張強(qiáng)度 | 80° | ASTM D-638 | 320 | kgf/cm2 |
| 彎曲彈性率 | 80° | ASTM D-790 | 7000 | kgf/cm2 |
| 斷裂下的伸張強(qiáng)度 | 23° | ASTM D-638 | 650 | kgf/cm2 |
| 屈服下的伸張強(qiáng)度 | -30° | ASTM D-638 | 870 | kgf/cm2 |
| 彎曲彈性率 | 23° | ASTM D-790 | 7500 | kgf/cm2 |
| 屈服下的延伸率 | 23° | ASTM D-638 | 8 | % |
| 彎曲彈性率 | 80° | ASTM D-790 | 4000 | kgf/cm2 |
| 彎曲彈性率 | -30° | ASTM D-790 | 36000 | kgf/cm2 |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 85 | |
| 彎曲強(qiáng)度 | 23° | ASTM D-790 | 400 | kgf/cm2 |
| 抗沖擊強(qiáng)度 | 23° | ASTM D-256 | 50 | kgf.cm/cm |
| 屈服下的伸張強(qiáng)度 | 80° | ASTM D-638 | 180 | kgf/cm2 |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 55 | |
| 抗沖擊強(qiáng)度 | -30° | ASTM D-256 | 4.0 | kgf.cm/cm |
| 彎曲強(qiáng)度 | 80° | ASTM D-790 | 250 | kgf/cm2 |
| 彎曲強(qiáng)度 | 23° | ASTM D-790 | 1100 | kgf/cm2 |
| 屈服下的伸張強(qiáng)度 | -30° | ASTM D-638 | 1100 | kgf/cm2 |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 120 | |
| 彎曲彈性率 | 23° | ASTM D-790 | 26000 | kgf/cm2 |
| 彎曲彈性率 | -30° | ASTM D-790 | 34000 | kgf/cm2 |
| 斷裂下的延伸率 | 23° | ASTM D-638 | 170 | % |
| 1%變形下的壓縮強(qiáng)度 | 23° | ASTM D-695 | 200 | kgf/cm2 |
| 屈服下的伸張強(qiáng)度 | 23° | ASTM D-638 | 750 | kgf/cm2 |
| 彎曲強(qiáng)度 | -30° | ASTM D-790 | 1400 | kgf/cm2 |
| 抗沖擊強(qiáng)度 | 23° | ASTM D-256 | 6.0 | kgf.cm/cm |
| 擠剪強(qiáng)度 | 23° | ASTM D-732 | 650 | kgf/cm2 |
| 斷裂下的延伸率 | 23° | ASTM D-638 | >200 | % |
| 1%變形下的壓縮強(qiáng)度 | 23° | ASTM D-695 | 100 | kgf/cm2 |
| 彎曲強(qiáng)度 | 80° | ASTM D-790 | 400 | kgf/cm2 |
| 介電常數(shù) | 103HZ | ASTM D-150 | 3.8 | |
| 絕緣耐力 | KV/mm | ASTM D-149 | 20 | |
| 介電常數(shù) | 106HZ | ASTM D-150 | 4.5 | |
| 介電常數(shù) | 60HZ | ASTM D-150 | 3.9 | |
| 介電常數(shù) | 106HZ | ASTM D-150 | 3.5 | |
| 抗電弧強(qiáng)度 | ASTM D-495 | 119 | S | |
| 介電損耗 | 60HZ | ASTM D-150 | 0.10 | |
| 介電常數(shù) | 60HZ | ASTM D-150 | 9.0 | |
| 介電損耗 | 103HZ | ASTM D-150 | 0.02 | |
| 介電損耗 | 103HZ | ASTM D-150 | 0.10 | |
| 介電損耗 | 60HZ | ASTM D-150 | 0.01 | |
| 體積電阻率 | ASTM D-257 | 1012 | Ω.cm | |
| IEC電路 | UL746 | 600+ | V | |
| 介電損耗 | 106HZ | ASTM D-150 | 0.02 | |
| 介電損耗 | 106HZ | ASTM D-150 | 0.12 | |
| 體積電阻率 | ASTM D-257 | 1015 | Ω.cm | |
| 介電常數(shù) | 103HZ | ASTM D-150 | 8.0 | |
| 熱變形溫度 | 4.6kgf/cm2 | ASTM D-648 | 175 | °C |
| 熔點(diǎn) | DSC | 215-225 | °C | |
| 熱變形溫度 | 18.6kgf/cm2 | ASTM D-648 | 75 | °C |
| 線性熱膨脹系數(shù) | ASTM D-696 | 8 | X的10-5cm/cm/°C | |
| 燃燒率 | UL94 | V-2 |
玻璃纖維增強(qiáng)型透明PA6樹脂工程料 日本宇部1013B