PBT SABIC VALOX Resin 310
| 產(chǎn)品型號： |
310 |
| 產(chǎn)品規(guī)格： |
PBT |
| 產(chǎn)品品牌： |
沙伯基礎(chǔ)創(chuàng)新塑料 |
公司自成立以來公司本著"質(zhì)量，信譽(yù)，價格合理;之宗旨開展經(jīng)營活動，業(yè)務(wù)遍布全國各地，深受廣大客戶歡迎。
美國沙伯基礎(chǔ)創(chuàng)新 PBT VALOX 310-1001,310-BK1066, 310,310SE0,312,315.325.注射成型,
|
|
|
Unreinforced, general purpose. Typical viscosity 5000-7000.
|
|
|
|
TYPICAL PROPERTIES (1)
|
|
MECHANICAL
|
Value
|
Unit
|
Standard
|
|
Tensile Stress, yld, Type I, 50 mm/min
|
520
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
520
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
300
|
%
|
ASTM D 638
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
840
|
kgf/cm2
|
ASTM D 790
|
|
Flexural Stress, brk, 1.3 mm/min, 50 mm span
|
840
|
kgf/cm2
|
ASTM D 790
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
23900
|
kgf/cm2
|
ASTM D 790
|
|
Hardness, Rockwell R
|
117
|
-
|
ASTM D 785
|
|
IMPACT
|
Value
|
Unit
|
Standard
|
|
Izod Impact, unnotched, 23°C
|
163
|
cm-kgf/cm
|
ASTM D 4812
|
|
Izod Impact, notched, 23°C
|
5
|
cm-kgf/cm
|
ASTM D 256
|
|
Gardner, 23°C
|
414
|
cm-kgf
|
ASTM D 3029
|
|
Modified Gardner, 23°C
|
414
|
cm-kgf
|
ASTM D 3029
|
|
THERMAL
|
Value
|
Unit
|
Standard
|
|
HDT, 0.45 MPa, 6.4 mm, unannealed
|
154
|
°C
|
ASTM D 648
|
|
HDT, 1.82 MPa, 6.4 mm, unannealed
|
54
|
°C
|
ASTM D 648
|
|
CTE, -40°C to 40°C, flow
|
8.1E-05
|
1/°C
|
ASTM E 831
|
|
CTE, 60°C to 138°C, flow
|
1.39E-04
|
1/°C
|
ASTM E 831
|
|
Relative Temp Index, Elec
|
120
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact
|
120
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact
|
140
|
°C
|
UL 746B
|
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
|
Specific Gravity
|
1.31
|
-
|
ASTM D 792
|
|
Specific Volume
|
0.76
|
cm3/g
|
ASTM D 792
|
|
Water Absorption, 24 hours
|
0.08
|
%
|
ASTM D 570
|
|
Mold Shrinkage, flow, 0.75-2.3 mm (5)
|
0.9 - 1.6
|
%
|
SABIC Method
|
|
Mold Shrinkage, flow, 2.3-4.6 mm (5)
|
1.5 - 2.3
|
%
|
SABIC Method
|
|
Mold Shrinkage, xflow, 0.75-2.3 mm (5)
|
1 - 1.7
|
%
|
SABIC Method
|
|
Mold Shrinkage, xflow, 2.3-4.6 mm (5)
|
1.6 - 2.4
|
%
|
SABIC Method
|
|
Melt Viscosity
|
6000
|
poise
|
SABIC Method
|
|
ELECTRICAL
|
Value
|
Unit
|
Standard
|
|
Volume Resistivity
|
>4.E+16
|
Ohm-cm
|
ASTM D 257
|
|
Dielectric Strength, in air, 1.6 mm
|
23.2
|
kV/mm
|
ASTM D 149
|
|
Dielectric Strength, in air, 3.2 mm
|
15.7
|
kV/mm
|
ASTM D 149
|
|
Dielectric Strength, in oil, 1.6 mm
|
23.2
|
kV/mm
|
ASTM D 149
|
|
Dielectric Strength, in oil, 3.2 mm
|
15.7
|
kV/mm
|
ASTM D 149
|
|
Relative Permittivity, 100 Hz
|
3.3
|
-
|
ASTM D 150
|
|
Relative Permittivity, 1 MHz
|
3.1
|
-
|
ASTM D 150
|
|
Dissipation Factor, 100 Hz
|
0.002
|
-
|
ASTM D 150
|
|
Dissipation Factor, 1 MHz
|
0.02
|
-
|
ASTM D 150
|
|
Arc Resistance, Tungsten {PLC}
|
5
|
PLC Code
|
ASTM D 495
|
|
High Voltage Arc Track Rate {PLC}
|
1
|
PLC Code
|
UL 746A
|
|
Comparative Tracking Index (UL) {PLC}
|
0
|
PLC Code
|
UL 746A
|
|
FLAME CHARACTERISTICS
|
Value
|
Unit
|
Standard
|
|
UL Recognized, 94HB Flame Class Rating (3)
|
1.47
|
mm
|
UL 94
|
|
Source GMD, last updated:2000/01/05
|
|
Parameter
|
|
Injection Molding
|
Value
|
Unit
|
|
Drying Temperature
|
120
|
°C
|
|
Drying Time
|
3 - 4
|
hrs
|
|
Drying Time (Cumulative)
|
12
|
hrs
|
|
Maximum Moisture Content
|
0.02
|
%
|
|
Melt Temperature
|
245 - 260
|
°C
|
|
Nozzle Temperature
|
240 - 255
|
°C
|
|
Front - Zone 3 Temperature
|
245 - 260
|
°C
|
|
Middle - Zone 2 Temperature
|
240 - 255
|
°C
|
|
Rear - Zone 1 Temperature
|
230 - 250
|
°C
|
|
Mold Temperature
|
50 - 75
|
°C
|
|
Back Pressure
|
0.3 - 0.7
|
MPa
|
|
Screw Speed
|
50 - 100
|
rpm
|
|
Shot to Cylinder Size
|
40 - 80
|
%
|
|
Vent Depth
|
0.013 - 0.025
|
mm
|
Source GMD, last updated:2000/01/05
|