| SABIC Innovative Plastics LNP STAT-KON Cycoloy_JK800 PC+ABS | |||
|---|---|---|---|
| Categories: |
Polymer; Thermoplastic; ABS Polymer; Polycarbonate/ABS Alloy, Carbon Fiber Filled; Polycarbonate (PC)
|
||
| Material Notes: |
LNP* Stat-kon* Cycoloy_JK800 compound is an 8% carbon fiber reinforcedPC+ABS, electrostatic dissipative ECO conforming FR. Good hydrolytic stability.
|
||
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. | ||
|
|||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow |
0.0010 - 0.0020 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0020 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse |
0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow |
17 g/10 min @Load 2.16 kg, Temperature 260 °C |
17 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
| 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
| 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.9 % | 1.9 % | Type I, 5 mm/min; ASTM D638 |
| 1.9 % | 1.9 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 1.9 % | 1.9 % | Type I, 5 mm/min; ASTM D638 |
| 1.9 % | 1.9 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 7.50 GPa | 1090 ksi | 1 mm/min; ISO 527 |
| 7.58 GPa | 1100 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 144 MPa | 20900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 145 MPa | 21000 psi | 2 mm/min; ISO 178 | |
| Flexural Yield Strength | 145 MPa | 21000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.20 GPa | 899 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 6.38 GPa | 925 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.47 J/cm | 6.50 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m2 | 1.90 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 21.0 kJ/m2 | 9.99 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy |
82.0 J @Temperature 23.0 °C |
60.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1000 ohm-cm | 1000 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+6 ohm | 1.00e+6 ohm | ASTM D257 |
| Static Decay | 0.010 sec | 0.010 sec | 5000V to <50V; FTMS101B |
| Thermal Properties | Metric | English | Comments |
CTE, linear, Parallel to Flow 
|
25.2 μm/m-°C @Temperature -40.0 - 40.0 °C |
14.0 μin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
|
26.0 μm/m-°C @Temperature 23.0 - 80.0 °C |
14.4 μin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
|
CTE, linear, Transverse to Flow
|
64.8 μm/m-°C @Temperature -40.0 - 40.0 °C |
36.0 μin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
|
74.0 μm/m-°C @Temperature 23.0 - 80.0 °C |
41.1 μin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) |
97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
Deflection Temperature at 1.8 MPa (264 psi)
|
92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
94.0 °C @Thickness 6.40 mm |
201 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 101 °C | 214 °F | Rate B/120; ISO 306 |
| 111 °C | 232 °F | Rate B/50; ASTM D1525 | |
| UL RTI, Electrical | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical with Impact | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | UL 746B |
|
Flammability, UL94
|
V-0 @Thickness 0.990 mm |
V-0 @Thickness 0.0390 in |
UL 94 |
|
5VB @Thickness 1.49 mm |
5VB @Thickness 0.0587 in |
UL 94 | |
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistent format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb'sterms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.
Users viewing this material also viewed the following:
SABIC Innovative Plastics Cycoloy? CX7211 PC+ABS
SABIC Innovative Plastics Cycoloy? C2951 PC+ABS
SABIC Innovative Plastics Cycoloy? C3650 PC+ABS
SABIC Innovative Plastics Cycoloy? C6600 PC+ABS
SABIC Innovative Plastics Cycoloy? CH6410 PC+ABS
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。
簡(jiǎn)繁切換