沙伯基礎(chǔ)創(chuàng)新塑料 PC+PBT 1102、1760T、5220U、5720U、6370、CL100、CL101、CL500U、X4820、X4830、X4850、X5300WX、XL1562、改良抗撞擊性,耐低溫撞擊,耐化學(xué)性良好,汽車(chē)領(lǐng)域的應(yīng)用
|
|
|
Unreinforced PC/polyester alloy. Excellent low temperatue impact/chemical resistance to automotive fluids.
|
|
|
|
TYPICAL PROPERTIES (1)
|
|
MECHANICAL
|
Value
|
Unit
|
Standard
|
|
Tensile Stress, yld, Type I, 50 mm/min
|
550
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
150
|
%
|
ASTM D 638
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
830
|
kgf/cm2
|
ASTM D 790
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
20000
|
kgf/cm2
|
ASTM D 790
|
|
Tensile Stress, yield, 50 mm/min
|
50
|
MPa
|
ISO 527
|
|
Tensile Stress, break, 50 mm/min
|
45
|
MPa
|
ISO 527
|
|
Tensile Strain, yield, 50 mm/min
|
4.5
|
%
|
ISO 527
|
|
Tensile Strain, break, 50 mm/min
|
115
|
%
|
ISO 527
|
|
Flexural Stress, yield, 2 mm/min
|
72
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min
|
1870
|
MPa
|
ISO 178
|
|
IMPACT
|
Value
|
Unit
|
Standard
|
|
Izod Impact, notched, 23°C
|
81
|
cm-kgf/cm
|
ASTM D 256
|
|
Izod Impact, notched, 0°C
|
70
|
cm-kgf/cm
|
ASTM D 256
|
|
Izod Impact, notched, -30°C
|
65
|
cm-kgf/cm
|
ASTM D 256
|
|
Izod Impact, notched 80*10*4 +23°C
|
54
|
kJ/m2
|
ISO 180/1A
|
|
Izod Impact, notched 80*10*4 0°C
|
52
|
kJ/m2
|
ISO 180/1A
|
|
Izod Impact, notched 80*10*4 -30°C
|
44
|
kJ/m2
|
ISO 180/1A
|
|
Charpy 0°C, V-notch Edgew 80*10*3 sp=62mm
|
50
|
kJ/m2
|
ISO 179/1eA
|
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
|
55
|
kJ/m2
|
ISO 179/1eA
|
|
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm
|
40
|
kJ/m2
|
ISO 179/1eA
|
|
Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
THERMAL
|
Value
|
Unit
|
Standard
|
|
HDT, 0.45 MPa, 6.4 mm, unannealed
|
110
|
°C
|
ASTM D 648
|
|
HDT, 1.82 MPa, 6.4 mm, unannealed
|
90
|
°C
|
ASTM D 648
|
|
CTE, -40°C to 40°C, flow
|
1.E-04
|
1/°C
|
ISO 11359-2
|
|
CTE, -40°C to 40°C, xflow
|
1.1E-04
|
1/°C
|
ISO 11359-2
|
|
Vicat Softening Temp, Rate A/50
|
155
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/120
|
120
|
°C
|
ISO 306
|
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
79
|
°C
|
ISO 75/Af
|
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
|
Specific Gravity
|
1.19
|
-
|
ASTM D 792
|
|
Specific Volume
|
0.83
|
cm3/g
|
ASTM D 792
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.8 - 1
|
%
|
SABIC Method
|
|
Mold Shrinkage, xflow, 3.2 mm (5)
|
0.8 - 1
|
%
|
SABIC Method
|
|
Density
|
1.19
|
g/cm3
|
ISO 1183
|
|
Melt Flow Rate, 250°C/5.0 kg
|
13
|
g/10 min
|
ISO 1133
|
|
Melt Volume Rate, MVR at 250°C/2.16 kg
|
6
|
cm3/10 min
|
ISO 1133
|
|
Melt Volume Rate, MVR at 250°C/5.0 kg
|
12
|
cm3/10 min
|
ISO 1133
|
|
Source GMD, last updated:2015/02/09
|
|
Parameter
|
|
Injection Molding
|
Value
|
Unit
|
|
Drying Temperature
|
110
|
°C
|
|
Drying Time
|
4 - 6
|
hrs
|
|
Drying Time (Cumulative)
|
8
|
hrs
|
|
Maximum Moisture Content
|
0.02
|
%
|
|
Melt Temperature
|
260 - 275
|
°C
|
|
Nozzle Temperature
|
255 - 270
|
°C
|
|
Front - Zone 3 Temperature
|
255 - 275
|
°C
|
|
Middle - Zone 2 Temperature
|
250 - 270
|
°C
|
|
Rear - Zone 1 Temperature
|
245 - 265
|
°C
|
|
Mold Temperature
|
65 - 90
|
°C
|
|
Back Pressure
|
0.3 - 0.7
|
MPa
|
|
Screw Speed
|
50 - 80
|
rpm
|
|
Shot to Cylinder Size
|
50 - 80
|
%
|
|
Vent Depth
|
0.013 - 0.02
|
mm
|
|
Source GMD, last updated:2015/02/09
|
 
轉(zhuǎn)載請(qǐng)注明：轉(zhuǎn)載自環(huán)球塑化資訊網(wǎng) http://56390.com.cn/news/
本文鏈接：http://56390.com.cn/index.php?homepage=&file=news&itemid=270030
免責(zé)聲明：本文"代理sabic沙特基礎(chǔ)創(chuàng)新塑料 PBT+PC XENOY?1102"僅代表作者個(gè)人觀(guān)點(diǎn)，與環(huán)球塑化網(wǎng)無(wú)關(guān)。環(huán)球塑化網(wǎng)所轉(zhuǎn)載的內(nèi)容，其版權(quán)均由原作者和資料提供方所擁有！如因作品版權(quán)問(wèn)題需要處理，請(qǐng)與我們聯(lián)絡(luò)。電話(huà)：400-115-2868
|
簡(jiǎn)繁切換