MFR 15 g/10 min; food contact quality; medium viscosity; easy release

Makrolon  2558

MVR (300 °C/1.2 kg) 14 cm3/10 min; medical devices; suitable for ETO and steam sterilization at 121 °C; biocompatible according to many ISO 10993-1 test requirements; medium viscosity; easy release

Makrolon  2600

MVR (300 °C/1.2 kg) 12 cm3/10 min; general purpose; medium viscosity

Makrolon  2605

MVR (300 °C/1.2 kg) 12 cm3/10 min; general purpose; medium viscosity; easy release

Makrolon  2607

MVR (300 °C/1.2 kg) 12 cm3/10 min; general purpose; medium viscosity; UV stabilized; easy release

Makrolon  2608

MVR (300 °C/1.2 kg) 12 cm3/10 min; medical devices; suitable for ETO and steam sterilization at 121 °C; biocompatible according to many ISO 10993-1 test requirements; medium viscosity

Makrolon  2652

MVR (300 °C/1.2 kg) 12 cm3/10 min; food contact quality; medium viscosity; easy release; complies with the BfR (formerly BgVV)- recommendations IX, XI and XLII abbr. the EN 71 part 3; toys

Makrolon  2656

MVR (300 °C/1.2 kg) 12 cm3/10 min; food contact quality; medium viscosity; easy release

    PC塑膠原料的吸水率較大，加工前一定要預(yù)熱干燥，純PC干燥120℃，改性PC一般用110℃溫度干燥4小時(shí)以上。干燥時(shí)間不能超過10小時(shí)。一般可用對空擠出法判斷干燥是否足夠。再生料的使用比例可達(dá)20%。在某些情況下，可的使用再生料，實(shí)際份量要視制品的品質(zhì)要求而定。再生料不能同時(shí)混合不同的色母粒，否則會(huì)嚴(yán)重?fù)p壞成品的性質(zhì)。

    PC塑料制品由于成本及其它方面的原因，多用改性材料，特別是電工產(chǎn)品，還須增加防火性能，在阻燃的PC和其它塑料合金產(chǎn)品成型時(shí)，對注塑機(jī)塑化系統(tǒng)的要求是混合好、耐腐蝕，常規(guī)的塑化螺桿難以做到，在選購時(shí)，一定要預(yù)先說明。

   PC是一種非晶體工程材料，具有特別好的抗沖擊強(qiáng)度、熱穩(wěn)定性、光澤度、抑制細(xì)菌特性、阻燃特性以及抗污染性。PC的缺口伊估德沖擊強(qiáng)度（otched Izod impact stregth）非常高，并且收縮率很低，一般為0.1%~0.2%。